Influence of deformation banding instabilities on small scale yielding of a Mg

Mar 23, 2023

Scientific Reports volume 13, Article number: 5767 (2023) Cite this article

681 Accesses

1 Altmetric

Metrics details

Propagating deformation bands are observed to accommodate the initial plasticity in an as-extruded Mg–1.5Nd alloy under tension using digital-image-correlation. The propagating bands cause an uncommon plateau in the stress–strain response of the alloy prior to restoring a common decreasing work hardening with further straining. Effects of the deformation banding and underlying plateau in the flow stress on small scale yielding are investigated during low cycle fatigue (LCF) and tension of notched specimens. Alternating formation/disappearance of deformation bands in the gauge section of as-extruded LCF specimens during testing is observed to reduce life compared to annealed specimens exhibiting no instabilities. In contrast, the bands deflect the plastic zone ahead of the notch from the principal plane orthogonal to the applied loading inducing positive effect on toughness of the alloy.

Alloys in which the so-called yield point phenomenon occurs exhibit a characteristic plateau stage i.e. an almost constant flow stress upon yielding1,2. Plastic deformation in the plateau takes place locally through instabilities such as in deformation bands, often termed as Lüders bands3,4. While such plastic instability phenomena are frequently observed in mild steels during tensile deformation5,6, they are less common in Mg alloys7,8,9. Traditionally, the inhomogeneous plastic flow in Mg alloys was largely associated with the avalanche of localized extension twining activity10,11. Twinning, as an important deformation mechanism in Mg, is dependent on the loading path relative to the grain crystal orientation12,13,14,15. Specifically, the deformation of highly textured Mg alloys in compression along the extrusion or rolling direction is dominated by extension twinning16,17,18. Twin cascades where twins in one grain stimulate twins in the neighboring grains across the grain boundary could also occur11,19,20,21,22. Since extension twinning causes little strain hardening in Mg alloys23,24,25,26, the occurrence of profuse twinning, also referred to as twin banding, could induce a plateau in the mechanical response27.

Instead of twinning, dislocation-induced plastic instability phenomena have recently been identified in some Mg alloys, specifically those containing rare earth elements7,9,28,29,30,31. Like in steels, the interaction between solute atoms and/or small precipitates and dislocations in Mg can strongly influence the flow behavior and can lead to plastic instabilities detectable at the macroscopic scale28. Although first described more than 150 years ago, the studies on plastic instabilities have mostly been carried out on steels32 and other body-centered cubic (bcc)33 metals. The number of studies on this subject in Mg alloys is limited. Given the growing interest in lightweight alloys34,35,36,37, it is now of interest to understand the nature and consequences of the plastic instability phenomena in Mg alloys.

The plastic instabilities are considered as undesirable phenomena during shaping operations because of surface irregularities they create known as stretcher-strains, Luders, or Hartman bands38. It remains to be determined whether any positive effects these instabilities might offer to the behavior of Mg alloys. In low-cyclic fatigue (LCF) tests, strain amplitudes are usually set below 3%39,40,41. In fracture toughness tests, the plastic zone ahead of the crack tip is used to assess the intrinsic toughness42. These two tests involve a small amount of plastic deformation and a localized plastic deformation, respectively. Since the plastic instability phenomena are likely to influence such small-scale yielding properties, this work here investigates LCF and toughness of the Mg–1.5Nd alloy exhibiting the observed phenomena28.

The alloy containing 1.5 wt.% Nd was cast conventionally, and then hot extruded at 300 ºC to bars of 12 mm diameter. While we used 99.95% purity of pure Mg to create the alloy, Table 1 details the composition of the alloy. Initial microstructure of the as-extruded alloy is provided in Fig. 1. The microstructure consists of equiaxed grains with an average grain size of ~ 4.3 μm predominantly oriented in a so-called ‘rare earth’ texture. More details on the microstructure derived from electron backscattered diffraction (EBSD), transmission electron microscopy (TEM), and synchrotron X-ray diffraction are provided in28. A few samples were subjected to short annealing at 375 °C for 15 min. The idea behind this annealing was to eliminate or at least minimize the effect of the shear band without compromise of yield strength. Since the annealing time was relatively short, it did not cause appreciable changes in the grain structure and texture compared to the as-extruded material. Therefore, a map of the annealed material is not provided. However, the annealing was sufficient to alter the solute clusters and metastable precipitates beyond the critical size to diminish the pinning of dislocations. Thus, the annealing step effectively eliminated the yield point phenomenon without compromising strength of the alloy. The dislocation pinning in the alloy is caused by small ~ 5 nm metastable precipitates and solute clusters as detailed in our earlier work18. The material was also annealed at 400 °C and at 485 °C for 15 min, 30 min, and 60 min and tested in tension to fracture. Results showed that the strength reduces with annealing temperature and annealing time.

Inverse pole figure (IPF) map showing the initial microstructure of Mg-1.5Nd alloy. The sample direction perpendicular to the maps is perpendicular to ED as indicated in the standard IPF triangle. The colors in the IPF maps represent the orientation of perpendicular to ED sample axis with respect to the crystal lattice frame according to the coloring in the standard IPF triangle.

Flat specimens with gauge section dimensions of 5.0 mm (L) × 4.0 mm (W) × 2.0 mm (T) and round specimens with gauge dimensions of 25.0 mm (L) × 7.0 mm (D) were cut from the extrusion bars using electric discharge machining (EDM) and turning, respectively. All specimens subsequently underwent grinding surface treatment of all sides consistently using SiC papers up to 1200 grit. Additionally, a notch with radius of 1 mm was machined in a set of flat specimens. The tests were repeated at least two times to ensure the results show sufficient similarity in the mechanical characteristics and observed phenomena. The loading axis was parallel to the extrusion direction (ED). Flat samples were tested using a Gatan micro-stage, while round samples were tested using a servo-hydraulic MTS machine Landmark 270. DIC was used to record the displacement/strain/strain-rate data. To this end, a speckle pattern was applied over the surfaces using Rust-Oleum spray paint with black dots on white background. Images were captured using Point Grey camera with fixed focal length lens and extension spacers to vary the total focal length. PointGrey FlyCap2 software was used for image recoding and VIC-2D v.6 was used for postprocessing the data. The strain rate was 0.001/s for all tests in the present work.

We begin with showing results of simple tension tests using the flat specimens coupled with a DIC system to characterize the deformation features of plastic instability phenomena. Figure 2a shows a typical stress–strain curve of the alloy during quasi-static tensile loading. Figure 2b magnifies the portion near yielding. A plateau stage can be seen from the stress–strain curve upon yielding, which is associated with the inhomogeneous deformation of the alloy. Figure 2c–f show strain fields recorded using DIC correlating the yielding and the deformation bands developing. Tongue-shaped strain localizations develop first in the region near transition from the grip section to the gauge section of the specimen while approaching the macroscopic yielding (Fig. 2d). Upon multiple such localizations (Fig. 2e), a band propagates through the entire width of the sample at ~ 45° to the loading direction connecting the localizations from the bottom to the top (Fig. 2e). Finally, the bend predominates rising the local strain to 0.012, while the rest of the localizations fades away.

(a) Stress–strain curve of the Mg–1.5Nd alloy along with (b) a magnified portion governed by the yielding point phenomena. (c–f) DIC strain fields (εyy) over the entire gauge section of the specimen in which the dashed ovals highlight tongue-shaped elasto-plastic strain localizations prior to the formation of a dominant deformation band.

As the images in Fig. 2d–f were recorded with known time resolution of 143 ms (ms), velocity of the band propagation was estimated. As the length of the band measured using DIC was about 6 mm, the velocity can then be estimated as 6 mm in 286 ms = 0.021 m/s. This value is at least one order of magnitude lower than the velocity of twin propagation, which was earlier established to be 0.1–10 m/s43. While both twinning and banding are shear deformations, the difference in velocities is attributed to the difference in scales of the phenomena. Twinning is a mechanism involving shear propagation though a single grain or sub-grain, while the band involves a cascade-like ‘unpinning’ of dislocations and collective propagation of shear though a polycrystalline aggregate as shown in28.

To illustrate the propagation of the band under tension, we present DIC strain-rate fields (dεyy/dt) in Fig. 3. The figure illustrates further development of the plastic instability upon formation. Evidently, the band propagates in both directions (Fig. 3c). The instantaneous fields show that the deformation occurs between the two fronts of the band (i.e. inside the band), while the rest of the material remains elastic. Nevertheless, the strain-rate at the fronts of the band is approximately two times higher than in the interior of the band. As the band takes over the entire gauge section (Fig. 3g), the alloy restores a common decreasing strain hardening rate with further plastic straining. Therefore, deformation within the plateau is accommodated by propagation of the band. As shown in28, the nucleation and propagation of the band has no interference with deformation twinning. The mechanism was primarily attributed to cascade unpinning of immobilized dislocations. Such behavior of dislocations results in nucleation and propagation of the band as shown on Figs. 2f and 3b–f respectively.

DIC strain rate fields (dεyy/dt) illustrating the development of plastic instabilities from (a) ε = 0 to (b) ε = 0.00183, (c) ε = 0.00188, (d) ε = 0.0045, (e) ε = 0.009, (f) ε = 0.01, (g) ε = 0.025, and (h) ε = 0.1.

Figure 4 compares strain fields developed under tension of an as-extruded sample versus a sample that underwent annealing. Annealing is known to eliminate the yield point phenomenon except in some ultrafine-grained or nano-grained materials produced by severe plastic deformation with grain sizes smaller than 1 µm44. The fields confirm that the non-annealed specimen deforms by a formation of a deformation band oriented ~ 45° relative to the loading direction, while the annealed specimen shows no formation of a deformation band but a regular strain localization in the middle of the gauge section due to the highest triaxiality at the center of the specimen.

DIC strain fields εyy under tension to ~ 0.01 true strain illustrating the differences in deformation between (a) as-extruded Mg–1.5Nd alloy and (b) annealed Mg–1.5Nd alloy at 375 °C for 15 min.

The role of deformation banding instabilities on small scale yielding of a Mg-Nd alloy is studied by carrying out LCF tests and tension of notched specimens. First, we explore the behavior of plastic instability under cyclic loading and its influence on LCF of the alloy. Figure 5 presents results of a fully reversed tension–compression LCF test for a non-annealed round specimen of Mg-1.5Nd alloy. The loading was applied with a strain amplitude of 0.0125. In Fig. 5a, the red curve corresponds to the first fully reversed cycle and the red letters b-e correspond to the DIC strain fields presented in Fig. 5b–e. The black curves in Fig. 5a correspond to subsequent cycles. The yield plateau appeared in both the first forward tension and the first reversed compression loadings, after which it disappeared. The annealed material shows no such plateau.

(a) Stress–strain curve recorded during cyclic tension–compression loading of the as-extruded alloy. DIC strain fields εyy during the 1st loading cycle: initial (b), at maximum tension (c), unloaded to 0 strain (d), and at maximum compression (e). DIC strain fields εyy at maximum tension (f) and at maximum compression (g) during the 1st, 2nd, and 10th cycles. Distributions of εyy strain along the gauge section of the specimen after the 1st, 2nd, and 10th cycles at (h) maximum tension and (i) at maximum compression.

The deformation band appeared at the lower part of the gauge section and propagated toward the other end, reaching a local maximum of ~ 0.02 tensile εyy strain (Fig. 5c,h). The band progressively faded during the unloading process to the point where it completely vanished (Fig. 5d). Upon the compression loading, a new compressive band formed in the top part of the sample reaching a similar local maximum of − 0.02 εyy strain (Fig. 5e,i). The alternating appearance of the tensile and compressive deformation bands during the following cyclic loadings repeated in a similar pattern (Fig. 5f,g), but the extent of such plastic instability was progressively waning. After the 10th cycle, the band is ‘stabilized’ and no longer reduces in maximum strain; the repetitive appearance and disappearance of the band is observed till the fracture of the sample. This unique cyclic deformation behavior, associated with the plastic instabilities, was not reported in previous studies. Interestingly, the localized behavior of the band observed by DIC is not reflected in the stress–strain cyclic curve from the 2nd cycle onwards as there is no yield plateau in the stress–strain curve.

The observed behavior results from dislocation glide in the materials that is responsible for the presence of yielding point phenomenon. On the first loading cycle, dislocations are pinned by the metastable precipitates, and their collective unpinning causes easy yielding. Regular ‘unpinned’ glide predominates from the second cycle. After unpinning during the first cycle, the dislocations likely shear over the same path again and again during the cyclic deformation so that the precipitates offer no pinning resistance to the glide of dislocations. Essentially, dislocations glide is increasingly easier with cycles because obstacles on the same path have been overcome during previous cycle.

A series of LCF tests involving three strain amplitudes were performed on annealed and non-annealed specimens of the alloy to assess the effect of plastic instabilities on life of the alloy. Results showing the LCF life are summarized in Table 2, while a more detailed table of parameters along with plots of stress-amplitudes are shown in the supplementary material of the paper. As can be seen, the non-annealed samples deforming with the plastic instabilities have fatigue life shorter for 20–60% compared to the annealed alloy, with larger difference at lower strain amplitudes. As shown in Fig. 5, the deformation bands cause straining of about half of the gauge section to about two times higher strain level than applied instead of spreading of the strain uniformly over the entire gauge section. The latter is normal behavior of the annealed material. With each cycle, the same region of specimen becomes highly strained repeatedly while the rest of the material remains elastic. An analogy can be drawn with a known effect of mean strain on fatigue life. For a given strain amplitude, fatigue life will be the lowest for a specimen cycled in only tension (mean strain is positive), followed by cycling with mean strain equal to 0 (fully reversed tension–compression), and the highest life will be for cycling in only compression (mean strain is negative)39,45. Therefore, the deformation behavior with plastic instabilities negatively influences the fatigue life given that a portion of the specimen experiences only tension.

To evaluate the effect of plastic instability on toughness of the alloy, tensile tests involving notched specimens of as-extruded and annealed alloy were performed. The load–displacement curves along with a comparison between the fields for the as-extruded versus annealed specimens are provided in Fig. 6. Figure 7 presents DIC strain fields εyy for the as-extruded specimen. Similar to the fields under tension of unnotched specimens, the formation of tongue-shaped elasto-plastic localizations were observed right before the band propagation. Strain localization ahead of the notch is expected, but the irregular and asymmetric shape of it is not typical42. Upon reaching yielding, the first band propagates on the side of the notch opposite to the location of the localization (Fig. 7). A load drop was observed from the load–displacement curve, which is followed by a short portion of linear hardening. As a result of such instabilities, a path of least resistance is deflected from the mode I principal plane orthogonal to the applied loading direction. Afterwards, the second shear band nucleates on the other side of a notch (Fig. 7d) causing another load drop and with further increasing of strain both bands grow in width. Once both bands are fully developed, the plastic zone ahead of the notch takes a relatively symmetric shape meaning that the alloy behaves in a common way with hardening followed by emerging and propagation of a crack at the later stage of deformation.

(a) Comparison of load–displacement (P-δ) curves recorded during tension of notched as-extruded and annealed specimens of the Mg–1.5Nd alloy. (b–e) DIC strain fields εyy illustrating the fields at the beginning of deformation (b, c) and at the beginning of crack nucleation (d, e). These are indicated by brackets in (a): as extruded specimens (left) and annealed specimens (right). Note the similarity of the strain fields in (d and e) with a slightly higher strain localization in the annealed specimen.

DIC strain fields (εyy) during tension of a notched specimen of as-extruded Mg–1.5Nd alloy at the following displacements (δ): (a) δ = 0, (b) δ = 0.075, (c) δ = 0.076, (d) δ = 0.125, (e) δ = 0.75, and (f) δ = 0.8.

The load–displacement curves of the notched specimens with and without annealing become overlapping after the initial yield portion confirming that the deformation banding phenomena affect primarily the early stage of the deformation near yielding. After the bands are fully propagated, the as-extruded alloy behaves like the annealed alloy without plastic instabilities. However, the crack nucleation in annealed alloy is observed earlier compared to the as-extruded alloy. Additionally, there is a slightly higher strain localization observed in the annealed specimen compared to the non-annealed one, which is more spread. Though these differences are not prominent, these can be signs of a positive effect of the bands on toughness. The property of toughness is traditionally considered to represent a combination of strength and ductility, the two properties that are mutually exclusive in general. The alloy used in the present study exhibiting an elongation of > 40% makes the yield point stage of about 2.5% insignificant in the whole plastic deformation. In contrast, if a much stronger but less ductile alloy is considered, a plastic instability could dominate the deformation and cause much larger effect on the properties, including substantial positive effect on toughness. In closing we indicate that even though the tests performed using notched specimens do not represent valid fracture toughness tests due to simplified sample geometry, the experiments performed here infer that equations of Continuum Fracture Mechanics would fail at describing the mechanical fields near the notch because of large asymmetry/heterogeneity driven by the instabilities.

In summary, we showed several novel experimental observations of plastic instabilities in a Mg alloy and evaluated their influence on the mechanical behavior of the alloy in a small-scale yielding regime. In particular, we observed the formation and propagation of localized deformation bands under tension of standard and notched specimens and cyclic loading. Nucleation of a deformation band under tension is preceded by a formation of tongue-shaped elasto-plastic strain localization heterogeneities. Upon nucleation, deformation bands propagate through the entire width of specimens, which is followed by the band widening with further straining. Under cyclic loading, the deformation band forms in tension but then disappears during unloading and a new band forms in a different region under compression. Such inhomogeneous deformation repeats during cyclic loading and adversely affects the fatigue life of the alloy. Nevertheless, the plastic instabilities deflect the plastic zone ahead of the notch from the principal plane orthogonal to the applied loading inducing some positive effect on the toughness of the alloy.

The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.

Khan, T., Rabinovitch, M., Stohr, J. F., Trottier, J. P. & Bibring, H. On the yield point phenomenon in composites. Scr. Metall. 7(7), 727–730. https://doi.org/10.1016/0036-9748(73)90122-1 (1973).

Article CAS Google Scholar

Van Petegem, S., Zimmermann, J. & Van Swygenhoven, H. Yield point phenomenon during strain rate change in nanocrystalline Ni–Fe. Scr. Mater. 65(3), 217–220. https://doi.org/10.1016/j.scriptamat.2011.04.007 (2011).

Article CAS Google Scholar

Schwab, R. & Ruff, V. On the nature of the yield point phenomenon. Acta Mater. 61(5), 1798–1808. https://doi.org/10.1016/j.actamat.2012.12.003 (2013).

Article ADS CAS Google Scholar

He, B. B., Liang, Z. Y. & Huang, M. X. Nanoindentation investigation on the initiation of yield point phenomenon in a medium Mn steel. Scr. Mater. 150, 134–138 (2018).

Article CAS Google Scholar

Liang, Z. Y., Cao, Z. H., Lu, J., Huang, M. X. & Tasan, C. C. Influence of co-existing medium Mn and dual phase steel microstructures on ductility and Lüders band formation. Acta Mater. 221, 117418. https://doi.org/10.1016/j.actamat.2021.117418 (2021).

Article CAS Google Scholar

Luo, H. et al. Interactions of nanoprecipitates, metastable austenite, and Lüders banding in an ultra-low carbon medium Mn steel with abnormal strength dependence of hydrogen embrittlement. Materialia 22, 101380. https://doi.org/10.1016/j.mtla.2022.101380 (2022).

Article CAS Google Scholar

Pei, R., Woo, S. K., Yi, S. & Al-Samman, T. Effect of solute clusters on plastic instability in magnesium alloys. Mater. Sci. Eng. A 835, 142685. https://doi.org/10.1016/J.MSEA.2022.142685 (2022).

Article CAS Google Scholar

Muransky, O., Barnett, M. R., Luzin, V. & Vogel, S. On the correlation between deformation twinning and Luders-like deformation in an extruded Mg alloy: In situ neutron diffraction and EPSC4 modelling. Mater. Sci. Eng. A-Struct. Mater. Prop. Microstruct. Process. 527(6), 1383–1394. https://doi.org/10.1016/j.msea.2009.10.018 (2010).

Article CAS Google Scholar

Bi, G. et al. Microstructure and yield phenomenon of an extruded Mg–Y–Cu alloy with LPSO phase. J. Rare Earths https://doi.org/10.1016/J.JRE.2022.01.011 (2022).

Article Google Scholar

Paudel, Y. et al. Characterization and modeling of 101¯ 2 twin banding in magnesium. Acta Mater. 183, 438–451 (2020).

Article ADS CAS Google Scholar

Barnett, M. R., Nave, M. D. & Ghaderi, A. Yield point elongation due to twinning in a magnesium alloy. Acta Mater. 60(4), 1433–1443 (2012).

Article ADS CAS Google Scholar

Xie, C. et al. Effect of local stresses of primary twinning on double twinning, twin intersection and their competition. Mater. Sci. Eng. A 769, 138498. https://doi.org/10.1016/j.msea.2019.138498 (2020).

Article CAS Google Scholar

Mokdad, F., Chen, D. L. & Li, D. Y. Twin-twin interactions and contraction twin formation in an extruded magnesium alloy subjected to an alteration of compressive direction. J. Alloys Compd. 737, 549–560. https://doi.org/10.1016/j.jallcom.2017.12.043 (2018).

Article CAS Google Scholar

Alam, M. E. et al. Rare-earth- and Aluminum-free, high strength dilute magnesium alloy. Sci. Rep. https://doi.org/10.1038/s41598-020-72374-z (2020).

Article PubMed PubMed Central Google Scholar

Tam, K. J. et al. Modelling the temperature and texture effects on the deformation mechanisms of magnesium alloy AZ31. Int. J. Mech. Sci. 182, 105727. https://doi.org/10.1016/j.ijmecsci.2020.105727 (2020).

Article Google Scholar

Beyerlein, I. J., Capolungo, L., Marshall, P. E., McCabe, R. J. & Tomé, C. N. Statistical analyses of deformation twinning in magnesium. Philos. Mag. 90(16), 2161–2190 (2010).

Article ADS CAS Google Scholar

Vasilev, E., Ferreri, N. C., Decker, R., Beyerlein, I. J. & Knezevic, M. Strain-rate sensitivity, tension-compression asymmetry, r-ratio, twinning, and texture evolution of a rolled magnesium alloy Mg–1.3Zn–0.4Ca–0.4Mn. Metall. Mater. Trans. A 51(8), 3858–3868. https://doi.org/10.1007/s11661-020-05841-x (2020).

Article CAS Google Scholar

Vasilev, E. & Knezevic, M. Role of microstructural heterogeneities in damage formation and fracture of oligocrystalline Mg under tensile loading. Mater. Sci. Eng. A https://doi.org/10.1016/j.msea.2021.142096 (2021).

Article Google Scholar

Chelladurai, I. et al. Modeling of trans-grain twin transmission in AZ31 via a neighborhood-based viscoplastic self-consistent model. Int. J. Plast. 117, 21–32. https://doi.org/10.1016/j.ijplas.2018.03.012 (2019).

Article CAS Google Scholar

Knezevic, M. et al. Deformation twinning in AZ31: Influence on strain hardening and texture evolution. Acta Mater. 58(19), 6230–6242 (2010).

Article ADS CAS Google Scholar

Jahedi, M., McWilliams, B. A., Kellogg, F. R., Beyerlein, I. J. & Knezevic, M. Rate and temperature dependent deformation behavior of as-cast WE43 magnesium-rare earth alloy manufactured by direct-chill casting. Mater. Sci. Eng. A 712, 50–64. https://doi.org/10.1016/j.msea.2017.11.092 (2018).

Article CAS Google Scholar

Jahedi, M., Ardjmand, E. & Knezevic, M. Microstructure metrics for quantitative assessment of particle size and dispersion: Application to metal-matrix composites. Powder Technol. 311, 226–238. https://doi.org/10.1016/j.powtec.2017.01.093 (2017).

Article CAS Google Scholar

Jahedi, M., McWilliams, B. A., Moy, P. & Knezevic, M. Deformation twinning in rolled WE43-T5 rare earth magnesium alloy: Influence on strain hardening and texture evolution. Acta Mater. 131, 221–232. https://doi.org/10.1016/j.actamat.2017.03.075 (2017).

Article ADS CAS Google Scholar

Feather, W. G., Savage, D. J. & Knezevic, M. A crystal plasticity finite element model embedding strain-rate sensitivities inherent to deformation mechanisms: Application to alloy AZ31. Int. J. Plast. 143, 103031. https://doi.org/10.1016/j.ijplas.2021.103031 (2021).

Article CAS Google Scholar

Feather, W. G. et al. Mechanical response, twinning, and texture evolution of WE43 magnesium-rare earth alloy as a function of strain rate: Experiments and multi-level crystal plasticity modeling. Int. J. Plast. 120, 180–204. https://doi.org/10.1016/j.ijplas.2019.04.019 (2019).

Article CAS Google Scholar

Savage, D. J. et al. Mechanical behavior and texture evolution of WE43 magnesium-rare earth alloy in split-Hopkinson pressure bar and Taylor impact cylinder testing. Int. J. Impact Eng. 143, 103589. https://doi.org/10.1016/j.ijimpeng.2020.103589 (2020).

Article Google Scholar

Anten, K. & Scholtes, B. Formation of macroscopic twin bands and inhomogeneous deformation during cyclic tension-compression loading of the Mg-wrought alloy AZ31. Mater. Sci. Eng. A 746, 217–228. https://doi.org/10.1016/j.msea.2019.01.033 (2019).

Article CAS Google Scholar

Wang, J. et al. Dislocation-induced plastic instability in a rare earth containing magnesium alloy. Materialia 15, 101038 (2021).

Article CAS Google Scholar

Li, R. G. et al. Room temperature yielding phenomenon in extruded or/and aged Mg–14Gd–2Ag–0.5Zr alloy with fine-grained microstructure. Mater. Sci. Eng. A 787, 139551. https://doi.org/10.1016/J.MSEA.2020.139551 (2020).

Article CAS Google Scholar

Jahedi, M., McWilliams, B. A. & Knezevic, M. Deformation and fracture mechanisms in WE43 magnesium-rare earth alloy fabricated by direct-chill casting and rolling. Mater. Sci. Eng. A 726, 194–207. https://doi.org/10.1016/j.msea.2018.04.090 (2018).

Article CAS Google Scholar

Ghorbanpour, S., McWilliams, B. A. & Knezevic, M. Effect of hot working and aging heat treatments on monotonic, cyclic, and fatigue behavior of WE43 magnesium alloy. Mater. Sci. Eng. A 747, 27–41. https://doi.org/10.1016/j.msea.2019.01.056 (2019).

Article CAS Google Scholar

Hall, E. O. Yield Point Phenomena in Metals and Alloys (Springer, 2012).

Google Scholar

Gaal, I., Tóth, A. L., Uray, L. & Harmat, P. Distinctive test for tungsten wires with different splitting properties. Int. J. Refract. Met. Hard Mater. 24(4), 325–331. https://doi.org/10.1016/J.IJRMHM.2005.10.005 (2006).

Article CAS Google Scholar

Ciach, R. (ed.)Vol. 59 (Springer, 1998). https://doi.org/10.1007/978-94-015-9068-6.

Book Google Scholar

Flower, H. M. Light alloys: Metallurgy of the light metals. Int. Mater. Rev. https://doi.org/10.1179/095066092790150876 (2012).

Article Google Scholar

Risse, M. et al. Elevated temperature effects on the plastic anisotropy of an extruded Mg-4 Wt Pct Li alloy: Experiments and polycrystal modeling. Metall. Mater. Trans. A 48(1), 446–458 (2017).

Article CAS Google Scholar

Nugmanov, D. et al. Origin of plastic anisotropy in (ultra)-fine-grained Mg–Zn–Zr alloy processed by isothermal multi-step forging and rolling: Experiments and modeling. Mater. Sci. Eng. A 713, 81–93. https://doi.org/10.1016/j.msea.2017.12.045 (2018).

Article CAS Google Scholar

Young, C. M., Walser, B., Abrahamson, E. P. II. & Sherby, O. D. Elimination of yield point phenomenon in mild steel by warm working. Scr. Metall. 9(1), 35–38 (1975).

Article CAS Google Scholar

Ghorbanpour, S., Mcwilliams, B. A. & Knezevic, M. Low-cycle fatigue behavior of rolled WE43-T5 magnesium alloy. Fatigue Fract. Eng. Mater. Struct. 42(6), 1357–1372 (2019).

Article CAS Google Scholar

Gribbin, S., Bicknell, J., Jorgensen, L., Tsukrov, I. & Knezevic, M. Low cycle fatigue behavior of direct metal laser sintered Inconel alloy 718. Int. J. Fatigue 93(Part 1), 156–167. https://doi.org/10.1016/j.ijfatigue.2016.08.019 (2016).

Article CAS Google Scholar

Ghorbanpour, S. et al. A crystal plasticity model incorporating the effects of precipitates in superalloys: Application to tensile, compressive, and cyclic deformation of Inconel 718. Int. J. Plast. 99(Supplement C), 162–185. https://doi.org/10.1016/j.ijplas.2017.09.006 (2017).

Article CAS Google Scholar

Ritchie, R. O. The conflicts between strength and toughness. Nat. Mater. 10, 817–822. https://doi.org/10.1038/NMAT3115 (2011).

Article ADS CAS PubMed Google Scholar

Vinogradov, A. et al. On the limits of acoustic emission detectability for twinning. Mater. Lett. 183, 417–419 (2016).

Article CAS Google Scholar

Liu, M. et al. Achieving excellent mechanical properties in type 316 stainless steel by tailoring grain size in homogeneously recovered or recrystallized nanostructures. Acta Mater. 226, 117629. https://doi.org/10.1016/j.actamat.2022.117629 (2022).

Article CAS Google Scholar

Dimatteo, N. D., & Lampman, S. R. ASM Handbook: Vol. 19 Fatigue and Fracture, (1996).

Download references

This research was sponsored by the U.S. National Science Foundation under the CAREER grant no. CMMI-1650641 and by the DEVCOM Army Research Laboratory under cooperative Agreement No. W911NF-21-2-0149.

Department of Mechanical Engineering, University of New Hampshire, Durham, NH, 03824, USA

Evgenii Vasilev & Marko Knezevic

National Engineering Research Center of Light Alloy Net Forming, Shanghai Jiao Tong University, Shanghai, 200240, China

Jie Wang & Gaoming Zhu

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

E.V. Methodology, Validation, Formal analysis, Investigation, Writing - Original Draft J.W. Methodology, Validation, Formal analysis, Investigation, Writing - Original Draft G.Z. Methodology, Investigation, Writing - Review & Editing M.K. Conceptualization, Methodology, Resources, Writing - Review & Editing, Supervision, Project administration, Funding acquisition.

Correspondence to Marko Knezevic.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Vasilev, E., Wang, J., Zhu, G. et al. Influence of deformation banding instabilities on small scale yielding of a Mg–Nd alloy revealed by in-situ digital image correlation. Sci Rep 13, 5767 (2023). https://doi.org/10.1038/s41598-023-33072-8

Download citation

Received: 01 December 2022

Accepted: 06 April 2023

Published: 08 April 2023

DOI: https://doi.org/10.1038/s41598-023-33072-8

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.